Based on a copolymer of vinyl chloride with vinyl acetate. Forms a uniform film of red-brown color without mechanical inclusions. Warranty period of storage – 6 months from the date of manufacture.
Purpose (XC-068) Designed for protection in complex multi-layer coating of equipment and metal structures from exposure to mineral acids and alkalis at temperatures up to 60 ° C, as well as under XB, XC enamels.
Application
Thoroughly clean dust and any other dirt or rust and degrease. Before applying the primer, mix thoroughly and dilute with solvent R-4 to a working viscosity of 12-14 seconds. viscometer type VZ-246 with a nozzle diameter of 4 mm at a temperature of (20 ± 2) ° C. The primer is applied by pneumatic spraying, brush, roller. An expense on 2 layers – 310 g / m ?.
Specifications (XC-068)
Name of the indicator | Value |
1. Film color | Red-brown shade is not normalized |
2. Appearance | After drying, the primer should form a uniform film of non-mechanical inclusions. |
3. Conditional viscosity by viscometer of the type VZ-246 with a nozzle diameter of 4 mm at a temperature of (20 ± 0.5) ° С, s | 30-70 |
4. Mass fraction of nonvolatile substances,% | 34 ± 3 |
5. Grinding degree, µm, not more than | 50 |
6. Drying time to degree 3 at a temperature of (20 ± 2) ° С, h, not more than | one |
7. Film hardness, pendulum device type TML (mA), onos. units, not less than | 0.2 |
8. Flexural elasticity of the film, mm, not more | one |
9. Film strength at impact on U-1 device, kgf · cm, not less | 50 |
10. Adhesion of film, points, not more | 3 |
11. Resistance of the film of the complex 4-layer coating at a temperature of (60 ± 2) ° C to the static effect of the solution, h, not less than: nitric acid with a mass fraction (25%) of sulfuric acid with a mass fraction (25%) of hydrochloric acid with mass share (20%)sodium hydroxide with a mass fraction (25%) |
12824 12 |
12. Film durability of a complex 4-layer coating to the static effect of nefras C3 80/120 at a temperature of (20 ± 2) ° С, hours, not less | 24 |