Products

Primer EP-076
September 3, 2018
Primer universal (deep impregnation)
September 3, 2018

Primer EP-45

Composition:
Primer based on epoxy resin with the addition of polyamide hardener. They are supplied in the form of two components – a semi-finished primer and hardener E-45. Primers in the coating system can be operated in a temperate and tropical climate, have high anti-corrosion and physico-mechanical properties. Can be applied to the surface to be painted by spraying, roller or brush. For primer EP-045T, application by airless spray is preferable. Primer EP-045T has a high resistance to runoff from a vertical surface, it can be applied with a thickness of 100-150 microns without the formation of drips wet on wet with an interlayer exposure time of 5-7 minutes. The consumption of primer EP-045 on a single-layer coating of 80 g / m ?, EP-045T-100g / m ?. 

Category:

Purpose (EP-45)
Primers are intended for priming metal surfaces of products in order to protect against corrosion. Used for priming products made of carbon steel, galvanized steel, aluminum and its alloys, copper, and during repairs. Primer EP-045 K is designed for priming the surface with residual rust.

Application
Перед применением полуфабрикат грунтовки тщательно перемешать, затем ввести отвердитель Э-45 в соотношении на 100 м.ч. полуфабриката грунтовки — 14 м.ч. отвердителя, выдержать грунтовку 30 мин. и разбавить до рабочей вязкости растворителем Р-5А или Р-5. Для нанесения методом пневматического распыления рабочая вязкость 15-20 с. по вискозиметру В3-246(сопло 4 мм). Кистью или валиком грунтовку наносить при выпускной вязкости, разбавлять при необходимости. Для безвоздушного распыления рабочая вязкость зависит от применяемого оборудования. При нанесении электростатическим напылением грунтовку разбавлять до рабочей вязкости 15-20сек. По вискозиметру В3-246(сопло 4 мм) разбавителем РЭ-4В. Жизнеспособность разбавленной до рабочей вязкости грунтовки с отвердителем не менее 6 ч при температуре (20±5)°С при условии хранения в плотно закрытой таре.

Technical characteristics (EP-45)

No The name of indicators Primer
EP-045
VC-045 “K” Primer EP-045 T
one. Film color Beige, tinted not standardized Beige tint is not standardized Beige, tint renormalized
2 The appearance of the film: After drying, the primer should form a uniform, flat surface without any inclusions.
four. Mass fraction of nonvolatile substances in the semifinished product of the primer,%: 66 ± 3 66 ± 3 66 ± 3
five. Primer milling degree mkm, not more: 40 40 40
6 Drying time to st 3 at a temperature of (20 ± 2) ° С, h, not more than 6 6 6
7 Film hardness by pendulum device type TML (pendulum A), relative units, not less 0.25 0.25 0.3
eight Flexural elasticity of the film, mm, not more one one one
9. Film durability at impact on the U-1 device, cm, not less 50 50 50
ten. Adhesion of film, points, not more one one one
eleven. Resistance of the primer film to static exposure at a temperature of (20 ± 2) ° С, h, at least, -water gasoline

-3% NaCl solution

14436048 14436022 14436048 
up