Enamel HS-75У
October 17, 2018
Enamel EP-140
October 17, 2018
Enamel HS-558
Type: Enamel is a suspension of titanium dioxide in a solution of a copolymer of vinyl chloride in organic solvents.
Scope: The enamel ХС-558 white is intended for coating the preliminary primed primer ХС-04 (TU 6-10-1414) of internal surfaces of metal and reinforced concrete tanks used for storing and transporting wine materials with an ethyl alcohol content of not more than 20%, as well as transportation and storage of drinking and industrial water.
Specifications:
| No | Name of the indicator | Requirements TNPA |
| one | Enamel coating color | White, shade is not standardized |
| 2 | The appearance of the enamel coating | After drying, it must be a smooth, uniform, without foreign inclusions surface. |
| 3 | The VZ-246 with a nozzle diameter of 4 mm (VZ-4) at a temperature of
(20.0 ± 0.5) ° С, s |
30 – 80 |
| four | Mass fraction of nonvolatile substances for enamel,% | 35 – 39 |
| five | Milling degree, µm, not more | thirty |
| 6 | Drying time to degree 3 at a temperature of
(20 ± 2) ° С, h, not more |
3 |
| 7 | Bending elasticity of the coating, mm, not more | one |
| eight | Adhesion of coating points | 2 |
| 9 | Coating hardness by pendulum device type TML (pendulum A), relative units, not less | 0.2 |
| ten | Co-ordinator of u-1, cm, not less | 50 |
| eleven | It is a temperature of (20 ± 2) ºС, h, not less | 2 |
| 12 | Resistance to water at a temperature of (20 ± 2) ºС, h, not less | 120 |
Benefits: Enamel provides a white semi-matt coating Complex coating with XC-04 primer and XC-558 enamel is resistant to minus 40 ºС to plus 60 ºС.
Surface preparation: Before using the HS-55 primer in accordance with TU 6-10-1414 on the HS-04 primer.
Application: P-4 or P-4A dilated with a solvent, it is thoroughly mixed with the HS-04 using a spraying temperature of 20 ° C. 2) ° C and relative humidity of not more than 70% in 4 layers (this is a layer of dried coating is 20–30 μm).
The air temperature can be reduced to no matter what the temperature is in the air.
The enamel is kept in water for at least 24 hours.
4-6 hours at a temperature of
(20 ± 2) ° C for 20–20 hours at a temperature of 60–80 ° C and does not contain moisture. 5% soda solution, then heated to 60 ° C with water, disinfected with 0.1% bleach solution and dried.
It is possible to apply enamel with a brush with an initial viscosity.
14 days with adequate ventilation.
For example, it can be used to ensure that it can be used at all times .
Storage: Enamel should be stored in a tightly closed container, protected from moisture and direct sunlight. Keep away from fire.
Precautionary measures: When carrying out the termination of the room carefully. Personal protection equipment (clothing, goggles and rubber gloves).
It doesn’t have a chemical effect.