Enamel PF-115 “M”
October 12, 2018
PF-115 “Lida Optima”
October 12, 2018

PF-115 “LIDA”

Type:  Enamel PF-115 “LIDA” is a suspension of pigments and fillers in pentaphthalic lacquer with the addition of solvents, desiccant and special additives.

Scope:  Enamel PF-115 “LIDA” is designed for painting metal, wood and other surfaces used indoors and in atmospheric conditions. Enamel is not a facade. 

Categories: , Tag:

Specifications

No The name of indicators Requirements TNPA
one Enamel coating color Must be established within the RAL color catalogs or control color samples.
2 The appearance of the coating After drying, it should be a smooth, homogeneous, without delamination, pock marks, wrinkles and foreign inclusions. Minor shagreen is allowed.
3 Of vz type 24 mm with a nozzle diameter of 4 mm, at a temperature of (20.0 ± 0.5) ° red, cherry, black
other colors
60 – 10080 – 120
four Milling degree, µm, not more 25
five Enamel drying time to degree 3 at a temperature of (20 ± 2) ° С, h, not more than red, cherry,
blackother colors
4824
24
6 Gloss of A Coating FB-2,%, not less 50
7 Flexural elasticity of the film, mm, not more one
eight Adhesion of film, points, not more one
9 Film durability U-1, cm, not less 40
ten The TML (pendulum A), rel. units, not less 0.1
eleven Resistance to a temperature of (20 ± 2) ° C, not lesson, h
transformer oil, h0.5% detergent solution, min
224
15

 

Advantages:  – The enamel coating forms a flat, smooth surface, provides a weatherproof, glossy coating; elastic, has good decorative and protective properties;

 

single-component enamel, stable during storage;

 

It is ideal for painting wooden surfaces (fences, grilles, fences, etc.);

 

The film is resistant to minus 50 ° C to plus 60 ° C

 

The Preparation : Wooden the Surfaces Applying the before the ENAMEL Should the BE cleaned up of resinous Substances, dried, polished and dedusted. It is recommended to be primed with GF-021, GF-021 “L” primer to improve its protective and decorative properties. It is necessary to remove the peeled-off coating, sand and dust the surface.

 

Before applying the enamel, metal surfaces should be thoroughly cleaned from dust, rust, scale and other contaminants (it is necessary to remove notches, burrs, welding spatter, round sharp edges, corners, teeth and welds; there should be no lubrication, marking paint and other substances, such as mineral contaminants, water-soluble salts that affect the quality of surface preparation), are sanded, degreased, dried and primed with primers GF-021 or GF-021 “L”, or GF-0119, or

GF-0119 “L”.

 

Previously painted surfaces must be cleaned from dust, grease, polish, degrease, dry and test paint. In the case of old coating, must be removed. The color of water should not be below 3 ° C.

 

For  enamel is thoroughly mixed, if necessary, diluted with nefras-C4-150 / 200

(TU RB 100006485.147), white spirit (GOST 3134) or a ratio of 25: 25% by weight of enamel. Enamel is applied in 1 – 2 layers with a brush, roller or spraying method. RE-4B or RE-3B. The thickness of the dried single-layer coating is not less than 20 microns.

 

It is a diluent liquid spraying, it is diluted with a 25 25 . Enamel can be applied with an initial viscosity.

 

24 hours at a temperature of (20 ± 2) ° C (except red, cherry) and a relative humidity of not more than 80%. It is increased. After the previous layer has dried. After staining, strong mechanical effects should not be avoided for 7 days.

 

The  surface of the painted surface, the application method, the enamel color, the personnel qualifications and other factors. 

 