Enamel PF-133
October 2, 2018PF-218 enamel
October 2, 2018
Enamel PF-167
Structure
Type: white, light gray. Glossy, weatherproof enamel PF 167 special purpose. Weatherproof, durable enamel with high adhesion to the painted surface and good interlayer adhesion.
The life of the coating on the basis of enamel PF 167 – 15 months. Shelf life – 12 months from the date of manufacture.
Purpose (PF-167)
PF 167 is intended to paint the outer surfaces of vessels of an unlimited navigation area, boats, metal, wooden and other surfaces exposed to weathering.
Application
Thinner White spirit, turpentine. Coating with a brush, roller, spray gun.
Drying time of a single-layer coating at a temperature (18-22) ° C – not more than 24 hours. Consumption of 60-80g enamel per 1 m? painted surface.
Specifications (PF-167)
| No | Name of the indicator | Value |
| one | Film color | Must be within the limits of permissible deviations established by samples of the “card index” or control samples of the color of JSC Lakokraska |
| 2 | The appearance of the film | After drying, the enamel should form a uniform, smooth, without delamination, pock marks, stains, wrinkles and foreign inclusions surface. |
| 3 | Enamel film gloss not less, (%) | 57 |
| four | Conditional viscosity according to the viscometer of the type VZ-246 with a nozzle diameter of 4 mm, at a temperature of (20.0 ± 0.5) ° C, not more than, (s) | 55-80 |
| five | Mass fraction of nonvolatile substances, (%) | 59-65 |
| 6 | Milling degree, not more, (µm) | 15 |
| 7 | Hookability of the dried film, (g / m?) | white – 75; light gray – 50 |
| eight | Drying time to degree 3 at a temperature of (20 ± 2) ° С, (h) | 24 |
| 9 | Enamel film elasticity at bending no more, (mm) | one |
| ten | Film durability at impact on the U-1 device not less, (cm) | 50 |
| eleven | Film hardness not less than by pendulum device type M-3 (standard units) | 0.2 |
| 12 | Adhesion of coating (points) | one |
| 13 | The resistance of the coating at a temperature of (20 ± 2) ° C to static effects, | water – 2.5 (h) |