Type : Varnish is a solution of a copolymer of vinyl chloride with vinyl acetate in a mixture of organic solvents with the addition of a plasticizer.
Scope : Varnish is used to paint the exterior surfaces of railway freight cars and tanks, equipment, metal and reinforced concrete structures exposed to solutions of mineral acids, alkalis, salts, corrosive gases (SO 2 , CO 2 , NO 2 , NH 3 ) and other chemical reagents with a temperature not exceeding 60 ° C, operated in atmospheric conditions of different climatic regions, as well as indoors.
The coating system and the service life of the coating are established for each aggressive medium in accordance with the regulatory and technical documentation for coloring certain types of products.
Specifications :
No | Name of the indicator | Lac
CH-724 |
one | Color of lacquer on iodine scale | 0.5 |
2 | Film color | – |
3 | The appearance of the film | Uniform, glossy, without wrinkles, craters, drips and foreign inclusions |
four | VZ-246 viscometer with a nozzle diameter of 4 mm (or VZ-4) at a temperature of (20.0 ± 0.5) ° C, s | 20 – 40 |
five | Mass fraction of nonvolatile substances,% | 22 ± 2 |
6 | Housing power of dried film, g / m 2 , not more than, for enamels: white light graygray |
––
– |
7 | Drying time (20 ± 2) ° С, h, not more than 3 degree to degree 4to degree 5 |
2–
24 |
eight | Flexural elasticity of the film, mm, not more | five |
9 | Grinding degree, µm, no more, for enamels: white light graygray primer |
––
– – |
ten | Adhesion, points, not more | – |
eleven | Film hardness by pendulum device M-3, conventional units, not less | 0.50 |
12 | Shelf life (viability) at a temperature of (20 ± 2) ° С, h, not less | – |
Advantages: Varnish is suitable for the environment.
Surface preparation for the painting on the product,
GOST 9.402 or STB ISO 12944-4.
Oil, grease, paint, dirt and other substances, such as mineral contaminants, water-soluble salts, It is necessary to remove incisions, burrs, welding spatters, round sharp edges, teeth and welding seams. It should be thoroughly cleaned, dust-free, degreased and dried. It is the most up to 3 cm wide range of residues from fluxes, alkaline slags and oxides formed during welding.
It is recommended to improve the protective properties of the surface oxides 1 – 2 according to GOST 9.402.
Application: before use, hardener no. 3 or hardener No. 5 is introduced into the example and enamels.
For a VZ-246 (or VZ-4), it is necessary to make it possible to adjust the temperature of (20.0 ± 0.5) ° C, use solvents P-4, P-4A according to
GOST 7827.
Lacquer spraying.
It can be seen that the consumer has been able to control the air flow rate (for example, air temperature, air temperature, air flow, air temperature, etc.).
It is not necessary to use heat in the process of heating.
24 hours.
There is no need for any method of cleaning the sanding surface.
The varnish consumption for a single-layer coating is 100 – 120 g / m² without taking into account the complexity of the painted surface, its preparation, application method, color, staff qualification and other factors.
Storage : Protected from sunlight and direct sunlight. Keep away from fire.
Precautionary measures associated with personal protective equipment (workwear, goggles, rubber gloves).
Finish, ventilate the room. It doesn’t have a chemical effect.