Enamel PF-133

Type:  Enamel PF-133 is a suspension of pigments and fillers in alkyd varnish with the addition of solvents, drying agent and special additives.

 

Scope:  PF-133 enamel is intended for painting freight rolling stock (except for refrigerated wagons), containers and other metal and wooden surfaces, except for agricultural machinery exposed to weathering.

 

P Advantages:

– enamel coating forms a flat, smooth surface, provides a glossy finish; elastic, possesses good decorative properties;

– single-component enamel, stable during storage, has excellent painting properties, which creates ease of use;

– enamel is ideal for painting wooden surfaces that do not require high performance characteristics: residential and residential wooden structures and fences, as well as metal surfaces (fences, grilles, fences, etc.). 

Categories: , Tag:

SPECIFICATIONS

 

The name of indicators Characteristic and norm
1. Enamel film color Red brown 652
2. Appearance of the coating After drying, it should be a smooth, homogeneous film, without “craters”, smudges, wrinkles and foreign inclusions.
3. Conditional viscosity on the VZ-246 viscometer with a nozzle diameter of 4 mm, at a temperature of (20.0 ± 0.5) ° C, s, 60 –130
4. Mass fraction of nonvolatile substances,% 55-62
5. Gloss of a coating on F-2, not less 45
6. Milling degree, µm, not more than 25
7. Hiding power of dried film, g / m 2 , not more than thirty
8. Drying time to degree 3 at a temperature of (82 ± 2) ° С, h, not more than
(20 ± 2) ° С, h, not more
1.5
thirty
9. Flexural elasticity of the film, mm, not more one
10. Film strength at-a-u type device, cm, not less 50
11. Film adhesion, points, not more one
12. Coating durability at temperature (20.0 ± 2) ° С, h, not less
industrial oil, h, not less
ten24
13. Film hardness by device device type: M-3, conventional units, not less 0.35

 

Surface preparation : Wooden surfaces before use should be cleaned of chemicals, dried, polished and dedusted. It is recommended to be primed with GF-021, GF-021 “L” primer to improve its protective and decorative properties. It is necessary to remove the peeled-off coating, sand and dust the surface.

Metal surfaces should not be thoroughly cleaned from dust, rust, rust, scalers, welding spatter, round edges, corners, teeth and welds; paint and other substances, such as mineral contamination, water-soluble salts, water-soluble salts), are sanded, degreased, dried and primed with primers GF-021 or GF-021 “L”, or GF-0119, or GF-0119 “L”.

Previously painted surfaces must be cleaned from dust, grease, polish, degrease, dry and test paint. In the case of old coating, must be removed. The color of water should not be below 3 ° C.

 

Coating:  Before use, it is thoroughly mixed, if necessary, dilute with nefras – C4-150 / 200 (TU RB 100006485.147), white spirit (GOST 3134) or a mixture of solvents with solvent (TU 38.101809) in a ratio Of 1: 1 in an amount not more than 30% by weight of enamel. RE-4B or RE-3B diluent is used. Enamel is applied in 1 – 2 layers with brush, roller, dipping or spraying methods (pneumatic, airless and in an electric field). The thickness of the dried single-layer coating is not less than 20 microns.

It is an enamel that has been diluted with a liquid that has been applied. weight of enamel. Enamel can be applied with an initial viscosity.

A single-layer drying coating is not more than 30 hours at a temperature of 2 ° C and a relative humidity of not more than 2 hours. than 80%. It is increased. After the previous layer has dried. After staining, strong mechanical effects should not be avoided for 7 days.

 

It has been  shown that it is possible to use a single layer coating for a surface coating, an application method, an enamel color, a personnel qualification and other factors. 

 